Jo augstāks alumīnija oksīda saturs, jo augstāka ugunsizturība; The content of calcium oxide increases with the decrease of aluminum oxide content. Adding aluminous cement as a binder in refractory castables can significantly shorten the demolding time within 24 hours. However, the addition of the aluminous cement can also affect the flowability of refractory castables and the process of construction and demolding, so improper use may have adverse effects on Construction .
The process of it can be divided into three stages: dissolution, nucleation, and precipitation. For example, the CA-50 is commonly used in the production of medium and low-grade refractory castables. However, it should be noted that CA-50 cement has the lowest strength at 800℃. Therefore, when the furnace odere tiek izmantota precīzi 800 grādu temperatūrā, ugunsizturīgo liešanas atlases atlasīšana kļūst īpaši sarežģīta, jo zemā temperatūra faktiski ierobežo parasto ugunsizturīgo liešanu . Šajā brīdī zemas cementa liešanas veidošanā kļūst par piemērotu izvēli, ar zemu kalcija saturu, lielisku stiprības veiktspēju vidējā temperatūrā un labu stiprumu vēlākai lietošanai .}}}}}}}}}}}}}}}}} {
Turpretī Ca {-70 un Ca {-80 augstajam alumīnija cementam ir augstāks alumīnija saturs un salīdzinoši mazāks papildinājuma attiecība .} ir piemēroti zemu cementa refraktīvo liešanu, kas ne tikai uzlabo izturību pret ugunsizturības, bet arī vairāk samazina kalcija saturu un uzlabo vidējo temperatūru {{{3}.
Rezumējot, pievienojot augsto alumīnija cementu ugunsizturīgajiem atlasāmiem, ir nepieciešams visaptveroši apsvērt savienošanas situāciju un darbības temperatūru . atbilstoši īpašām prasībām, izvēlieties pievienot Ca -50 vai Ca -70 un Ca -80}, lai nodrošinātu optimālu reaktīvo kastu veiktspēju .}}}}}}}}}}}}}}}}}}}}}}}} Organis „Orgling” kopsummu kopsvecklnesis kopsēji ”